Tungsten Trioxide Specifications
Volframi trioksiidi spetsifikatsioonidas following:
| Hinne | WO 3 (%, min) | Lisandid (%, max) | |||||||
| Al | As | Bi | Ca | Mg | Cu | K | Na | ||
| WO3-1 | 99.95 | 0.0005 | 0.001 | 0.0001 | 0.0015 | 0.0005 | 0.0003 | 0.001 | 0.001 |
| WO3-2 | 99.5 | 0.0015 | 0.01 | -- | 0.01 | 0.01 | -- | 0.005 | 0.005 |
| Impurities(%,max ) | ||||||||||
| Fe | Mn | Mo | Ni | P | Pb | S | Sb | Si | Sn | Ti |
| 0.001 | 0.0005 | 0.002 | 0.0007 | 0.0007 | 0.0001 | 0.0007 | 0.0003 | 0.001 | 0.0001 | 0.001 |
| 0.04 | -- | 0.03 | -- | 0.004 | -- | 0.006 | -- | 0.005 | -- | -- |
| Grade | WO3 (%,min ) | Apparent Density(g/cm3) | Fess((Fsss.)u | 目數(mesh) 100% |
| WO3-1 | 99.95 | 2~2.8 | 7~16 | -40 |
| WO3-2 | 99.5 | 0.6~1.0 | 0.6~1.5 |
Seotud tooted:
Ammooniummetatungstate (AMT) on volframhüdrometallurgilise protsessi oluline vaheühend, v?limus on valge kristalne pulber, lahustuvus vees on suurim volframiühendites, mis on üle 300 g WO3 / 100 ml H2O (25 ℃).
Tungstiinhape viitab volframtrioksiidi, WO3 hüdraatunud vormidele. K?ige lihtsam vorm, monohüdraat, on WO3H2O, samuti on teada dihüdraat WO3 · 2H2O. WO3 · H2O tahke oleku struktuur koosneb oktaedriliselt koordineeritud WO5 (H2O) üksuste kihtidest, kus jagatakse 4 tippu.
Sinine volframoksiid viitab tume sinise ühendi klassile, mis sisaldab volframit (Ⅵ) ja volframi (V) segaventiilsust. Sinine volframoksiid on redutseerivate ja volframiühendite produkt. Sinise volframoksiidi koostis on keeruline, mille hulgas on ka vaheühendeid, nagu n?iteks WO2 ja W4.
Cesium volfram pronks on anorgaaniline nano materjal, millel on hea omadus, mis neelab ühtlase tera suuruse ja dispergeeruvusega peaaegu infrapuna, millel on tugeva neeldumisfunktsiooniga infrapunapiirkonnas lainepikkusega 800 ~ 1200nm. 380 ~ 780 nm.